Secondary battery and method of manufacturing the secondary battery

ABSTRACT

A secondary battery and a method of manufacturing the same are disclosed. In one embodiment, the secondary battery includes an electrode assembly including an external surface, an electrolyte, a sealing tape including an adhesive layer attached to at least portion of an outer surface of the electrode assembly and contacting the external surface of the electrode assembly and a base sheet disposed on an adhesive layer and formed of a material having directionality, and a can receiving the electrode assembly, the electrolyte, and the sealing tape, wherein the base sheet loses directionality and is shrunk and deformed in shape by contact with the electrolyte, and at least portion of the base sheet contacts an inner surface of the can to prevent the electrode assembly from being freely moved within the can.

RELATED APPLICATIONS

This application claims priority to and the benefit of ProvisionalPatent Application No. 61/241,768 filed on Sep. 11, 2009 in the U.SPatent and Trademark Office, the entire contents of which areincorporated herein by reference.

This application also relates to U.S. patent application Ser. Nos.12/554,528 and 12/554,504, both filed on Sep. 4, 2009, both of which areincorporated herein by reference in their entirety.

BACKGROUND

1. Field

Embodiments relate to a secondary battery and a method of manufacturingthe same.

2. Description of the Related Technology

Generally, an electrode assembly together with an electrolyte isreceived into a can to form a secondary battery. The electrode assemblyincludes a positive electrode plate, a negative electrode plate, and aseparator disposed between the positive and negative electrode plates.

SUMMARY

One aspect is a secondary battery configured to prevent an electrodeassembly from being freely moved in a can and a method of manufacturingthe same.

Another aspect is a secondary battery including: an electrode assemblyincluding an external surface; an electrolyte; a sealing tape includingan adhesive layer attached to at least portion of an outer surface ofthe electrode assembly and contacting the external surface of theelectrode assembly and a base sheet disposed on an adhesive layer andformed of a material having directionality; and a can receiving theelectrode assembly, the electrolyte, and the sealing tape, wherein thebase sheet loses directionality and is shrunk and deformed in shape bycontact with the electrolyte, and at least portion of the base sheetcontacts an inner surface of the can.

The base sheet may include a first region in which a thickness of atleast portion of the base sheet increases and a second region in which athickness of at least portion of the base sheet decreases when the basesheet is shrunk by contacting the electrolyte, and the base sheetcontact the inner surface of the can in the first region in which athickness of at least portion of the base sheet increases.

The base sheet may include a thermal shrinkage film under a temperatureof about 30° C. or more. The shrinkage of the base sheet may be about40% or more, and particularly, range from about 40% to about 64%. In thebase sheet 51, shrinkage in a transverse direction (TD) may be greaterthan that in a machine direction (MD). The base sheet may have athickness of about 20 um to 60 um. The base sheet may have a thicknessof about 20 um to 300 um in the first region. The base sheet may beshrunk and deformed by contacting the electrolyte and is separated fromthe adhesive layer.

The base sheet may be formed of oriented polystyrene (Hereinafter,referred to as a shrinkable OPS) having a shrinkage characteristic. Theelectrolyte may include a non-aqueous organic solvent which isconfigured to remove the directionality of the base layer. Thenon-aqueous organic solvent may include a carbonate based non-polarorganic solvent. The carbonate based non-polar organic solvent mayinclude one of dimethyl carbonate (DMC) electrolyte, diethyl carbonate(DEC) and dipropyl carbonate (DPC). The sealing tape may be wound arounda quarter or more of the outer surface of the electrode assemblyincluding the finishing part.

Another aspect is a method of manufacturing a secondary battery, themethod including: preparing an electrode assembly including an externalsurface, a sealing tape including an adhesive layer attached to at leastportion of an outer surface of the electrode assembly and contacting anexternal surface of the electrode assembly and a base sheet disposed onthe adhesive layer and formed of a material having directionality, and acan receiving the electrode assembly and the sealing tape; attaching thesealing tape to at least portion of the electrode assembly to insert theelectrode assembly and the sealing tape into the can; and injecting anelectrolyte into the can such that the base sheet loses itsdirectionality by contacting an electrolyte and is shrunk and deformed,and at least portion of the base sheet contacts an inner surface of thecan.

After the injection process is performed, the method of manufacturingthe secondary battery may further include at least one of a formationprocess and an aging process. The aging process may be performed byexposing the assembled battery to an environment having a temperaturefrom about 50° C. to about 70° C. for about 18 hours to about 36 hours.The base sheet may be shrunk and deformed by contacting the electrolyteand be separated from the adhesive layer, and after the aging process isperformed, the adhesive layer may have an adhesion force ranging fromabout 2 kgf/cm² to about 9 kgf/cm².

Another aspect is a secondary battery, comprising: an electrode assemblycomprising an outer surface; an electrolyte; a sealing tape attached toand surrounding at least part of the outer surface of the electrodeassembly, wherein the sealing tape comprises i) an adhesive layercontacting the outer surface of the electrode assembly and ii) a baselayer formed on the adhesive layer, and wherein the base layer is formedof a material which has directionality; and a can accommodating theelectrode assembly and sealing tape, wherein the base layer, uponcontacting the electrolyte, is configured to at least partially losedirectionality and partially shrink so that at least a portion partiallyincreases thickness.

In the above battery, the adhesive layer, upon contacting theelectrolyte, is configured to not substantially deform so as to maintainthe adhesive property thereof. In the above battery, the adhesive layerhas an adhesion force ranging from about 2 kgf/cm² to about 9 kgf/cm².

In the above battery, at least a portion of the base layer is thickerthan at least a different portion of the base layer, and wherein thethicker portion of the base layer contacts an inner surface of the can.In the above battery, the electrolyte comprise at least one of thefollowing: dimethyl carbonate (DMC), diethyl carbonate (DEC), dipropylcarbonate (DPC), methylpropylcarbonate (MPC), ethylpropyl carbonate(EPC), methylethyl carbonate (MEC), ethylene carbonate (EC), propylenecarbonate (PC), and butylene carbonate (BC).

In the above battery, the base layer has a thickness in the range ofabout 20 μm to about 60 μm. In the above battery, the thickness of theadhesive layer is in the range of about 1 μm to about 30 μm. In theabove battery, the adhesive layer comprises an acryl-based adhesivematerial, and wherein the acryl-based adhesive material comprises atleast one of the following: poly methyl methacrylate (PMMA), poly ethylmethacrylate (PEMA), and poly butyl methacrylate (PBMA).

Another aspect is a secondary battery, comprising: an electrode assemblycomprising an outer surface; an electrolyte; a sealing tape attached toand surrounding at least part of the outer surface of the electrodeassembly, wherein the sealing tape comprises i) an adhesive layercontacting the outer surface of the electrode assembly and ii) a baselayer formed on the adhesive layer; and a can accommodating theelectrode assembly and sealing tape, wherein the base layer comprisesfirst and second regions, wherein the first region is thicker than thesecond region, and wherein the first region contacts an inner surface ofthe can.

In the above battery, the thickness of the first region of the baselayer is in the range of about 20 μm to about 300 μm. In the abovebattery, the base layer comprises at least one of the following:polystyrene (PS), polyamide, polyacrylonitrile, polyvinyl alcohol,polycarbonate, polyethylene vinyl acetate, and oriented polystyrene(OPS). In the above battery, the adhesive layer, upon contacting theelectrolyte, is configured to not substantially deform so as to maintainthe adhesive property thereof. In the above battery, the adhesive layerhas an adhesion force ranging from about 2 kgf/cm² to about 9 kgf/cm².

Another aspect is a method of manufacturing a secondary battery,comprising: providing 1) an electrode assembly comprising an outersurface, 2) a sealing tape attached to and surrounding at least part ofthe outer surface of the electrode assembly, wherein the sealing tapecomprises i) an adhesive layer contacting the outer surface of theelectrode assembly and ii) a base layer formed on the adhesive layer,wherein the base layer is formed of a material which has directionalityand wherein the base layer comprises first and second regions, and 3) acan configured to receive the electrode assembly and sealing tape;placing the electrode assembly and the sealing tape into the can so asto form an assembled secondary battery; and subjecting the base layer tocontact electrolyte, wherein the base layer at least partially losesdirectionality and partially shrink so that the first region is thickerthan the second region and contacts an inner surface of the can.

In the above method, the shrinkage of the base layer in an axialdirection is greater than that in a winding direction, and wherein theaxial direction is substantially perpendicular to the winding direction.In the above method, the shrinkage of the base layer is about 40% ormore with respect to the base layer before contacting the electrolyte.In the above method, the shrinkage of the base layer is in the range ofabout 40% to about 64% with respect to the base layer before contactingthe electrolyte. In the above method, the shrinkage of the base layer ina axial direction is in the range of about 50% to about 70%, and whereinthe shrinkage of the base layer in a winding direction is in the rangeof about 0% to about 5%. In the above method, the base layer has athermal shrinkage characteristic under a temperature of about 30° C. Inthe above method, the electrolyte comprise at least one of thefollowing: dimethyl carbonate (DMC), diethyl carbonate (DEC), dipropylcarbonate (DPC), methylpropylcarbonate (MPC), ethylpropyl carbonate(EPC), methylethyl carbonate (MEC), ethylene carbonate (EC), propylenecarbonate (PC), and butylene carbonate (BC).

In the above method, the base layer comprises a shrinkable orientedpolystyrene (OPS) film. In the above method, the shrinkable OPS film ismanufactured using an elongation process. In the above method, theshrinkable OPS film has a shrinkage of about 40% or more. In the abovemethod, a longitudinal elongation of the OPS film is over about 45% anda transverse elongation of the OPS film is over about 210%.

The above method further comprises performing at least one of aformation process and an aging process. In the above method, the agingprocess is performed by exposing the assembled battery to an environmenthaving a temperature from about 50° C. to about 70° C. for about 18hours to about 36 hours. In the above method, the adhesive layer, uponcontacting the electrolyte, does not substantially deform so as tomaintain the adhesive property thereof, and wherein the adhesive layerhas an adhesion force ranging from about 2 kgf/cm² to about 9 kgf/cm².

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates a perspective view of a secondary battery accordingto an embodiment.

FIG. 2 illustrates an exploded perspective view of the secondary batteryof FIG. 1.

FIG. 3 illustrates a longitudinal sectional view of the secondarybattery of FIG. 1.

FIG. 4 illustrates a partially schematic cross-sectional view of thesecondary battery of FIG. 1 before an electrolyte is injected into thesecondary battery.

FIG. 5 illustrates a schematic perspective view of an electrode assemblyof FIG. 1 after an electrolyte is injected into the secondary battery.

FIG. 6 illustrates a longitudinal sectional view of the secondarybattery after an electrolyte is injected into the secondary battery.

FIG. 7 illustrates a schematic perspective view of a secondary batterybefore an electrode assembly contacts an electrolyte according toanother embodiment.

FIG. 8 is a magnified photograph (×30) of an OPS film of ComparativeExample 2 according to Experimental Example 3.

FIG. 9 is a magnified photograph (×30) of an OPS film of Example 1according to Experimental Example 3.

DETAILED DESCRIPTION

Secondary batteries may be classified into a cylinder type secondarybattery and a prismatic type secondary battery. In the cylinder typesecondary battery, a cylindrical electrode assembly is received into acylindrical can. The cylindrical electrode assembly received into thecylindrical can may be easily rotated or slipped relative to thecylindrical can due to external vibrations or impacts. Such relativemovement may increase the internal resistance of the secondary batteryand damage electrode tabs of the electrode assembly, and thus it isdesirable to prevent the electrode assembly from being rotated orslipped relative to the cylindrical can.

Exemplary embodiments will now be described more fully hereinafter withreference to the accompanying drawings; however, they may be embodied indifferent forms and should not be construed as limited to theembodiments set forth herein. Rather, these embodiments are provided sothat this disclosure will be thorough and complete, and will fullyconvey the scope of the invention to those skilled in the art.

Referring to FIGS. 1 to 6, a secondary battery 5 according to anembodiment includes a can 10, an electrode assembly 20, a lowerinsulating member 30, an upper insulating member 40, a sealing tape 50,an electrolyte, and a cap assembly 100.

The can 10 may have a cylindrical shape and be formed of a lightconductive metal such as aluminum or an aluminum alloy. In anotherembodiment, the secondary battery 5 may be other type secondary battery.For example, the cross-section of the secondary battery has a polygonalshape. For convenience, a cylinder type secondary battery will bedescribed.

The can 10 may be manufactured using a machining process such as deepdrawing. In one embodiment, the can 10 has a cylindrical shape and isformed of a light conductive metal such as aluminum or an aluminumalloy. The can 10 may have a different shape depending on the shape ofthe electrode assembly 20. For convenience, a cylindrical can will bedescribed. Referring to FIG. 3, the can 10 includes a circular bottomplate 12 and a cylindrical sidewall 13 extending from an edge of thecircular bottom plate 12. A beading part 15 protruding inwardly alongthe periphery of the can 10 is formed on an upper portion of thesidewall 13. The beading part 15 prevents the lower insulating member30, the electrode assembly 20, and the upper insulating member 40 frombeing moved from the inside of the can 10 toward a directionsubstantially perpendicular to the bottom plate 12. A crimping part 16is disposed on a top end of the sidewall 13. The crimping part 16provides sealing between the can 10 and the cap assembly 100. An opening10 a is defined in a top portion of the sidewall 13 so that the lowerinsulating member 30, the electrode assembly 20, the upper insulatingmember 40, and the cap assembly 100 are sequentially inserted into thecan 10 through the opening 10 a.

The electrode assembly 20 includes a first electrode plate 21, a secondelectrode plate 23, a first separator 25 a, and a second separator 25 b.The electrode assembly 20 further includes a first electrode tab 27 aand a second electrode tab 27 b. In one embodiment, the first electrodeplate 21, the first separator 25 a, the second electrode plate 23, andthe second separator 25 b are sequentially stacked, and then,cylindrically wound to form the electrode assembly 20.

In this embodiment, the first electrode plate 21 includes a positiveelectrode plate, and the second electrode plate 23 includes a negativeelectrode plate. In another embodiment, the second electrode plate 23may be a positive electrode plate and the first electrode plate 21 maybe a negative electrode plate.

In one embodiment, although not shown in detail, the first electrodeplate 21 includes a positive electrode collector and a positiveelectrode coating portion. The positive electrode collector may beformed of a conductive metal to collect electrons from the positiveelectrode coating portion and deliver the electrons to an externalcircuit. The positive electrode coating portion may be formed of atleast one of a positive electrode active material, a conductivematerial, and a binder. The positive electrode coating portion may becoated on the positive electrode collector. First non-coating portionson which the positive electrode coating portion is not coated may bedisposed on both ends of a winding direction of the first electrodeplate 21. In one embodiment, the first electrode tab (positive electrodetab) 27 a is coupled to one of the first non-coating portions using amethod such as welding. The first electrode tab 27 a extends from theinside of the can 10 toward the opening 10 a.

In one embodiment, although not shown in detail, the second electrodeplate 23 includes a negative electrode collector and a positiveelectrode coating portion. The negative electrode collector may beformed of a conductive metal to collect electrons from the negativeelectrode coating portion and deliver the electrons to an externalcircuit. The negative electrode coating portion may be formed of atleast one of a negative electrode active material, a conductivematerial, and a binder. The negative electrode coating portion may becoated on the negative electrode collector. Second non-coating portionson which the negative electrode coating portion is not coated may bedisposed on both ends of a winding direction of the second electrodeplate 23. In one embodiment, the second electrode tab (negativeelectrode tab) 27 b is coupled to one of the first non-coating portionsusing a method such as welding. The first electrode tab 27 a extendsfrom the inside of the can 10 toward the bottom plate 12. In oneembodiment, the second electrode tab 27 b is coupled to the bottom plate12 of the can 12 using a method such as welding. In this embodiment, thecan 10 has a negative polarity, and the bottom plate 12 of the can 10 isused as a negative terminal of the secondary battery 5.

The first and second separators 25 a and 25 b allow the first and secondelectrode plates 21 and 23 to be separated from each other. Fine poresmay be formed in the first and second separators 25 a and 25 b. As aresult, lithium ions moving between the first and second electrodeplates 21 and 23 may pass through the fine pores. Each of the first andsecond separators 25 a and 25 b may be formed of a polymer resin such aspolyethylene (PE) and polypropylene (PP).

The lower insulating member 30 may have an approximate disk shape toprovide insulation between the electrode assembly 20 and the bottomplate 12 of the can 10. The upper insulating member 40 may have anapproximate disk shape to provide insulation between the electrodeassembly 20 and the beading part 15 of the can 10.

In one embodiment, the sealing tape 50 is attached to at least portionof an outer surface of the electrode assembly 20. In one embodiment, thesealing tape 50 includes an adhesive layer 52 contacting an outersurface of the electrode assembly 20 and a base sheet (or base layer) 51disposed on the adhesive layer 52 and formed of a material havingdirectionality.

The sealing tape 50 is attached to the outer surface of the woundelectrode assembly 20 to prevent the electrode assembly 20 from beingunwound, by the use of a finishing part 20 a formed on the outer surfacethereof. In one embodiment, the outermost end of the second separator 25b is placed at the finishing part 20 a. The sealing tape 50 may beattached to the electrode assembly 20 in a manner such that the sealingtape 50 is wound around the outer surface of the electrode assembly 20including the finishing part 20 a. Therefore, it may prevent theelectrode assembly 20 from being unwound.

The sealing tape 50 may be wound once around the outer surface of theelectrode assembly 20 when the sealing tape 50 is attached to the outersurface of the electrode assembly 20. The sealing tape 50 may be woundmultiple times around the outer surface of the electrode assembly 20.Alternatively, the sealing tape 50 may be wound around only a portion ofthe electrode assembly 20 in the circumferential direction of theelectrode assembly 20. For effectively preventing movement of theelectrode assembly 20 relative to the can 10, the sealing tape 50 may bewound one or more times around the outer surface of the electrodeassembly 20.

The sealing tape 50 is disposed between the outer surface of theelectrode assembly 20 and the inner surface of the can 10. Here, asurface of the sealing tape 50 facing the inner surface of the can 10may have low frictional resistance such that the electrode assembly 20is easily inserted into the can 10.

The base sheet 51 may be a polymer film that loses its directionality bycontacting the electrolyte, and thus, the base sheet 51 may be shrunkand varied in shape. In one embodiment, when the polymer film contactsthe electrolyte, a non-aqueous organic solvent of the electrolyte ispermeated between molecules of the polymer film, and thus, thedirectionality of the polymer film, which is formed during thefabrication process of the polymer film, may be lost, and the polymerfilm is shrunk. Here, the directionality of the polymer film may begenerated by, for example, uniaxial drawing, biaxial drawing, andcompression, which is applied during a film manufacturing process usinga resin.

In one embodiment, the base sheet, upon contacting the electrolyte, maypartially shrink and partially expand. For example, the base sheet 51may include a first region in which a thickness of at least portion ofthe base sheet 51 increases and a second region in which a thickness ofat least portion of the base sheet 51 decreases when the base sheet 51is shrunk by contacting the electrolyte. The first region in which thethickness of the base sheet 51 increases may contact an inner surface ofthe can 10. Thus, when the first region in which the thickness of thebase sheet 51 increases contacts the inner surface of the can 10, africtional force is generated to prevent the electrode assembly 20 frombeing freely moved.

Shrinkage of the base sheet 51 caused by an aging process of thesecondary battery (hereinafter, simply referred to as a “shrinkage”) maybe about 40% or more, and particularly, range from about 40% to about64%. The shrinkage is a resultant value measured after the base sheet 51is left in a thermostat bath containing the non-aqueous organic solventthat loses the directionality of the base sheet 51 at about 60° C. forabout 24 hours. The non-aqueous organic solvent will be described later.The above range (about 40% or more) may effectively and/or efficientlyprevent movement of the electrode assembly 20. However, depending on theembodiments, the shrinkage of the base sheet 51 may be less than about40%.

Here, in the shrinkage of the base sheet 51, shrinkage in a transversedirection (TD) or axial direction may be greater than that in a machinedirection (MD) or a winding direction. In one embodiment, the shrinkagein the MD may approach almost zero.

In order to obtain the base sheet 51 having shrinkage of about 40% toabout 64%, a thermal shrinkage of the base sheet 51 in the TD may rangefrom about 70% to about 50%, and a thermal shrinkage of the base sheet51 in the MD may range from about 0% to about 5%, but are not limitedthereto. Here, the thermal shrinkage is a resultant value measured aftera film constituting the base sheet 51 is left in the thermostat bath atabout 90° C. for about 10 seconds.

Since the base sheet 51 may be variably modified according to standardtypes of battery, the base sheet 51 may have a thickness ranging fromabout 20 μm to about 60 μm, but is not limited thereto. The above range(about 20 μm to about 60 μm) may effectively and/or efficiently preventmovement of the electrode assembly 20. However, depending on theembodiments, the base sheet 51 may have a thickness less than about 20μm or greater than about 60 μm.

As above-described, the base sheet 51 loses its directionality, and thusis shrunk and deformed when the base sheet 51 contacts the electrolyte.Due to such deformation, the first region in which the film increases inthickness is formed. In the first region in which the film increases inthickness, the film may have a thickness ranging from about 20 um toabout 300 um. When the thickness of the film is within the above rangein the first region, the movement preventing effect of the electrodeassembly may be maximized.

The base sheet 51 may be formed of any polymer film as long as thepolymer film may lose its directionality formed during a fabricationprocess (such as uniaxial drawing, biaxial drawing, or compression), andthus be shrunk and deformed in shape by contact with electrolyte. Thebase sheet 51 may include at least one of the following: a polystyrene(PS) film, a polyamide film, a polyacrylonitrile film, a polyvinylalcohol film, a polycarbonate film, a polyethylene vinyl acetate film,and an oriented polystyrene (OPS) film, which may be easily penetratedby the non-aqueous organic solvent of electrolyte because of itsrelatively large intermolecular distance.

Among the above-described films, a film having a thermal shrinkagecharacteristic under a temperature of about 50° C. or more may be usedas the base sheet 51. When the film having the thermal shrinkagecharacteristic is used, the base sheet 51 may be significantly changedin thickness due to the thermal shrinkage in the aging process oftypical processes of manufacturing the secondary battery 5. Thus, thebase sheet 51 may further firmly contact the inner surface of the can 10in the first region in which the thickness of the base sheet increasesto efficiently prevent the electrode assembly 20 from being freelymoved.

A shrinkable OPS film may be used as the base sheet 51. In thisembodiment, an OPS film represents a general OPS film manufactured usingan injection molding process. The shrinkable OPS film represents an OPSfilm manufactured using an elongation process. A shrinkable OPS filmhaving shrinkage of about 40% or more has relatively high elongation.According to an embodiment, when a longitudinal elongation is over about45%, and a transverse elongation is over about 210%, a shrinkable OPSfilm having shrinkage of about 40% or more may be obtained. Theshrinkable OPS film having shrinkage within the above range may have avery uniform thickness when compared to the general OPS filmmanufactured using the injection molding process. Also, in theshrinkable OPS film having shrinkage within the above range, a foreignsubstance (a foreign substance of the OPS film used for this embodimentrepresents a gel) is reduced in thickness when compared to the generalOPS film manufactured using the injection molding process. This is donebecause a gel thickness is conserved into a raw condition as it is inthe OPS film manufactured using the injection molding process, but a gelthickness is reduced due to the elongation process in the OPS filmmanufactured using the elongation process.

In one embodiment, the adhesive layer 52 is coated on the base sheet 51and contacts the finishing part 20 a formed on the outer surface of thewound electrode assembly 20. The adhesive layer 52 may be formed of anyadhesive material that is generally used for a sealing tape 50 in therelated art and may not react with the electrolyte. For example, theadhesive layer 52 may be formed by coating the base sheet 51 with anacryl-based adhesive. The acryl-based adhesive may be an adhesiveselected from the group consisting of poly methyl methacrylate (PMMA),poly ethyl methacrylate (PEMA), and poly butyl methacrylate (PBMA).

The adhesive layer 52 may be coated on the base sheet 51 using variouscurrently available coating methods, and the thickness of the adhesivelayer 52 may be varied. For example, the adhesive layer 52 may be coatedto a thickness of about 1 μm to about 30 μm by coating the base sheet 51with an adhesive through a knife coating process. However, the basesheet 51 may be coated to a different thickness using another coatingmethod.

The sealing tape 50 may be attached to the electrode assembly 20 in amanner such that the entire width of the electrode assembly 20 isenclosed by the sealing tape 50. Alternatively, the sealing tape 50 maybe attached to the electrode assembly 20 except for an upper end part 20b and a lower end part 20 c of the outer surface of the electrodeassembly 20 as shown in FIG. 2. An electrolyte may be permeated betweenthe can 10 and the electrode assembly 20 through the upper end part 20b, and the electrolyte injected into a bottom of the can 10 may contactthe electrode assembly 20 at the lower end part 20 c. Therefore, whenimmersion of the electrode assembly 20 in the electrolyte is considered,the sealing tape 50 may not be attached to the upper end part 20 b andthe lower end part 20 c. In this embodiment, the width of the sealingtape 50 is not limited to a specific value. However, the width of thesealing tape 50 may be equal to or greater than about 20% of the widthof the electrode assembly 20. The above range (equal to or greater thanabout 20%) may effectively and/or efficiently prevent movement of theelectrode assembly 20. However, depending on the embodiments, the widthof the sealing tape 50 may be less than about 20% of the width of theelectrode assembly 20. The sealing tape 50 may further sequentiallyinclude an auxiliary adhesive layer and an auxiliary base sheet (notshown) between the base sheet 51 and the adhesive layer 52. Here, thebase sheet 51 loses its directionality by contacting the electrolyte andis shrunk. Thus, at least a portion of the base sheet 51 contacts theinner surface of the can 10, and the auxiliary adhesive layer isdisposed below the base sheet 51. Also, the adhesive layer 52 contactsthe outer surface of the electrode assembly 20, and the auxiliary basesheet is disposed between the adhesive layer 52 and the auxiliaryadhesive layer. As described above, when the auxiliary adhesive layerand the auxiliary base sheet are further provided, it may moreefficiently prevent the electrode assembly from being released bydeformation due to the shrinkage of the base sheet 51. Here, anolefin-based film used for a general sealing tape may be used as theauxiliary base sheet, and an adhesive having the same material as thatof the adhesive layer 52 may be used as the auxiliary adhesive layer.

Any electrolyte may be used as long as the electrolyte includes anon-aqueous organic solvent by which the base sheet 51 may be shrunk,and the directionality of a polymer film may be released. For example,the non-aqueous organic solvent may include carbonates. Examples of suchcarbonates include dimethyl carbonate (DMC), diethyl carbonate (DEC),dipropyl carbonate (DPC), methylpropylcarbonate (MPC), ethylpropylcarbonate (EPC), methylethyl carbonate (MEC), ethylene carbonate (EC),propylene carbonate (PC), and butylene carbonate (BC). The non-aqueousorganic solvent may include a carbonate-based non-polar organic solvent.For example, the carbonate based non-polar organic solvent may includeat least one of dimethyl carbonate (DMC), diethyl carbonate (DEC), anddipropyl carbonate (DPC). Such a carbonate based non-polar organicsolvent may be easily permeated between molecules of a polymer such aspolystyrene (PS) having a relatively large intermolecular distance, sothat the directionality of the polymer can be easily released. Thecarbonate based non-polar organic solvent of the non-aqueous organicsolvent, i.e., at least one of the DMC, DEC, and DPC may include about10% to about 60% by weight of the total contents of the electrolyte. Theabove range (about 10% to about 60%) may effectively and/or efficientlyprevent movement of the electrode assembly 20. However, depending on theembodiments, the electrolyte may include less than about 10% or morethan about 60% by weight of the total contents of the electrolyte.

Other commercially available electrolytes except for the organic solventmay be used as the electrolyte according to an embodiment. That is, thenon-aqueous organic solvent, specifically, the carbonate based non-polarorganic solvent, specifically, any electrolyte including the DMC, theDEC, or the DPC may be used as the electrolyte according to anembodiment.

The cap assembly 100 is disposed between the crimping part 16 and thebeading part 15. The cap assembly 100 includes a safety vent 110, acurrent interrupt device (CID) 120, a positive temperature coefficient(PTC) device 130, and a cap-up 140 that are disposed in this order awayfrom the electrode assembly 20.

The safety vent 110 electrically connects the first electrode tab 27 aand the CID 120. The safety vent 110 includes a protrusion 112 at acentral portion thereof. The protrusion 112 may be convex toward theelectrode assembly 20 and electrically connected to the first electrodetab 27 a. When the inside pressure of the secondary battery 5 exceeds areference pressure, the protrusion 112 may be reversed. The CID 120electrically connects the safety vent 110 and the PTC device 130. Whenthe protrusion 112 is reversed due to an increased inside pressure ofthe secondary battery 5, the CID 120 may be broken so that the safetyvent 110 and the PTC device 130 may be electrically disconnected.

The electric resistance of the PTC device 130 may increase steeply asthe surrounding temperature increases. The PTC device 130 electricallyconnects the CID 120 and the cap-up 140. When the temperature of thesecondary battery 5 increases excessively, the electric resistance ofthe PTC device 130 may increase greatly to interrupt the current flow.

In one embodiment, the cap-up 140 is electrically connected to the PTCdevice 130 and exposed to the outside of the secondary battery 5. Thecap-up 140 may be used as a positive terminal of the secondary battery5.

The cap assembly 100 is insulated from the can 10 by an insulatinggasket 150. The insulating gasket 150 is disposed around thecircumference of the cap assembly 100 and fixed to the inside of the can10 by the beading part 15 and the crimping part 16.

The structure of the cap assembly shown in the drawings is an exemplarystructure provided for describing an embodiment. The structure of thecap assembly 100 can be variously changed. It will be apparent to thoseof ordinary skill in the art that the structure of the cap assemblyshown in the drawings may be changed or modified without departing fromthe spirit and scope of the present invention.

FIG. 7 illustrates a schematic perspective view of a secondary batterybefore an electrode assembly contacts an electrolyte according toanother embodiment. Referring to FIG. 7, a secondary battery includes anelectrode assembly 20 and a sealing tape 50 including an adhesive layer52 attached to at least portion of an outer surface of the electrodeassembly 20 and contacting an external surface of the electrode assembly20 and a base sheet 51 disposed on the adhesive layer 52 and formed of amaterial having directionality. Since the electrode assembly 20 and thesealing tape 50 have the same structure as those of the secondarybattery 5 illustrated in FIGS. 1 to 6 except for winding degree of thesealing tape 50 a, duplicated descriptions will be omitted. However,only the winding degree of the sealing tape 50 a will be described indetail.

The sealing tape 50 is attached to the outer surface of the woundelectrode assembly 20 to prevent the electrode assembly 20 from beingunwound. That is, the electrode assembly 20 includes a finishing part 20a on the outer surface thereof. The outermost end of the secondseparator 25 b may be placed at the finishing part 20 a. The sealingtape 50 is attached to the electrode assembly 20 in a manner such thatthe sealing tape 50 is wound around the outer surface of the electrodeassembly 20 including the finishing part 20 a. Therefore, it may preventthe electrode assembly 20 from being unwound.

Here, the sealing tape 50 may be wound to cover only a portion of alongitudinal direction of the outer surface of the electrode assembly 20including the finishing part 20 a on the outer surface of the electrodeassembly 20. When considering the movement of the electrode assembly 20,the sealing tape 50 may be wound around about a quarter or more of theouter surface of the electrode assembly 20 including the finishing part20 a on the outer surface of the electrode assembly 20. The above range(about a quarter or more) may effectively and/or efficiently preventmovement of the electrode assembly 20. However, depending on theembodiments, the sealing tape 50 may be wound around about a quarter orless of the outer surface of the electrode assembly 20.

A method of manufacturing a secondary battery will now be described withreference to FIGS. 1 to 6. A method of manufacturing a secondary battery5 includes a preparation process, an assembly process, and an injectionprocess. Depending on the embodiments, additional processes may beadded, others removed, or the order of the processes changes.

In the preparation process, an electrode assembly 20, a sealing tape 50,and a can 10 are prepared. The electrode assembly 20 includes anexternal surface. The sealing tape 50 includes an adhesive layer 52attached to at least portion of an outer surface of the electrodeassembly 20 and contacting an external surface of the electrode assembly20 and a base sheet 51 disposed on the adhesive layer 52 and formed of amaterial having directionality. The can 10 receives the electrodeassembly 20 and the sealing tape 50. Since the components used in thepreparation process are previously described above, their detaileddescriptions will be omitted.

In the assembly process, the sealing tape 50 is attached to at leastportion of the electrode assembly 20, and then, the electrode assembly20 and the sealing tape 50 are inserted into the can 10. The sealingtape 50 is disposed between the outer surface of the electrode assembly20 and the inner surface of a can 10. In the assembly process, theelectrode assembly 20 to which the sealing tape 50 is attached isinserted in the can 10, and other components of a secondary battery 5are assembled.

In detail, a lower insulating member 30, the electrode assembly 20 towhich the sealing tape is attached, and an upper insulating member 40are sequentially arranged from a lower side. In this state, a secondelectrode tab 27 b of the electrode assembly 20 is coupled to a bottomplate 12 of the can 10 by a method such as welding. At this time, abeading part and a crimping part are not yet formed at the can 10. Next,the lower insulating member 30, the electrode assembly 20 to which thesealing tape 50 is attached, and the upper insulating member 40 aresequentially inserted into the can 10 through an opening 10 a of the can10. Thereafter, a beading part 15 is formed at a sidewall 13 of the can10 so that the lower insulating member 30, the electrode assembly 20 towhich the sealing tape 50 is attached, and the upper insulating member40 may be stably held in the can 10 without movement substantiallyperpendicular to the bottom plate 12.

In the injection process, the base sheet 51 loses its directionality bycontacting an electrolyte, and thus is shrunk and deformed. Theelectrolyte is injected into the can 10 such that at least portion ofthe base sheet 51 contacts an inner surface of the can 10. Theelectrolyte allows lithium ions generated by an electrochemical reactionin electrodes 25 a and 25 b when charged and discharged to be movable.

When the electrolyte is injected, the electrolyte contacts the basesheet 51 of the sealing tape 50 attached to the outer surface of theelectrode assembly 20. At this time, a non-aqueous organic solvent ofthe electrolyte is penetrated between molecules due to the contactbetween the base sheet 51 and the electrolyte to lose the directionalityapplied to the base sheet 51 during a film fabrication process.

When the directionality is lost, the base sheet 51 is shrunk to form afirst region in which at least portion of the base sheet 51 increases inthickness and a second region in which at least portion of the basesheet 51 decreases in thickness. The base sheet 51 contacts the innersurface of the can 10 in the first region in which at least portion ofthe base sheet 51 increases in thickness to prevent the electrodeassembly 20 from being freely moved inside the can 10.

A finishing assembly process may be performed after the electrolyte isinjected. An insulating gasket 150 is inserted through the opening 10 aand placed on the beading part 15. Thereafter, a cap assembly 100 isplaced inside the insulating gasket 150. Then, a crimping part 16 isformed on the upper end of the sidewall 13 so as to fix the insulatinggasket 150 and the cap assembly 100. After the secondary battery 5 isassembled in this way, a post-treatment operation such as a formationoperation and an aging operation may be performed.

In the formation operation, the assembled secondary battery 5 may berepeatedly charged and discharged so as to activate the secondarybattery 5. When the secondary battery 5 is charged, lithium ions movesfrom a lithium metal oxide used as a positive electrode to a carbonelectrode used as a negative electrode. At this time, since lithium ishighly reactive, the lithium ions react with the negative carbonelectrode to produce reaction products such as Li2, CO3, LiO, and LiOHwhich form a film called solid electrolyte interface (SEI) on thesurface of the carbon electrode.

In the aging operation, the secondary battery 5 may be allowed to sitfor a predetermined time so as to stabilize the SEI film. For example,in the aging operation, the secondary battery 5 may be allowed to sitfor about 18 hours to about 36 hours at about 50° C. to about 70° C.

At this time, when the base sheet 51 having a thermal shrinkagecharacteristic is used, the base sheet 51 is left at a high temperaturefor a long time during the aging process. Thus, thermal shrinkage isadditionally progressed to sufficiently shrink the base sheet 51 of thesealing tape 50. Due to the thermal shrinkage, the base sheet 51 of thesealing tape 50 is sufficiently deformed to form locally thicker parts,and thus movement of the electrode assembly 20 relative to the can 10may be effectively prevented by the locally thicker parts of the basesheet 51.

The base sheet 51 is shrunk and deformed by contacting the electrolyte,and thus is separated from the adhesive layer 52. This is done becausethe base sheet 51 may be substantially significantly deformed to exertadhesion (detachable) characteristics of an adhesive, thereby beingseparated from the adhesive layer 52. Thus, the adhesive layer 52 ismaintained in a state in which the adhesive layer 52 is attached to theelectrode assembly 20. According to this embodiment, after the agingprocess is performed, the adhesive layer 52 has an adhesion forceranging from about 2 kgf/cm² to about 9 kgf/cm². When an adhesion forceof the adhesive layer 52 remains after the aging process is performed,it may prevent the electrode assembly 20 from being released.

The adhesion force is obtained by measuring a force at a time point atwhich upper and lower ends of the secondary battery 5 are cut, and apush-pull gauge is disposed on the lower end of the secondary battery 5,and then, the push-pull gauge is pushed upwardly to move the electrodeassembly 20.

Hereinafter, certain examples according to exemplary embodiments will bedescribed. However, the present disclosure is not limited to suchexamples.

Example 1

LiCoO2 used as a positive electrode active material, polyvinylidenefluoride (PVDF) used as a binder, and carbon used as a conductivematerial were mixed at a weight ratio of 92:4:4, and the mixture wasdispersed in N-methyl-2-pyrrolidone so as to form a positive electrodeslurry. The positive electrode slurry was coated with an aluminum foilhaving a thickness of about 20 μm and was dried and rolled to form apositive electrode.

Artificial graphite used as a negative electrode active material,styrene-butadiene rubber used as a binder, and carboxymethylcelluloseused as a thickener were mixed at a weight ratio of 96:2:2, and themixture was dispersed in water so as to form a negative electrodeslurry. A copper foil having a thickness of about 15 μm was coated withthe negative electrode slurry and was dried and rolled to form anegative electrode.

A polyethylene/polypropylene porous film (Hoest Cellanese, U.S.) havinga thickness of 20 μm was used as a separator. The separator was placedbetween the cathode and the anode. Then, the separator, the cathode, andthe anode were wound, and a sealing tape was wound around them tomanufacture an electrode assembly.

A 35 μm (±0.03 μm) thickness shrinkable polystyrene (OPS) film(elongation: TD 45%, MD 210%, shrinkage: 52%, thermal shrinkage: TD 66%,MD 5%) coated with a 15 μm thickness poly methyl methacrylate (PMMA)adhesive was used as the sealing tape.

The electrode assembly wound by a jelly-roll method was inserted in acylindrical aluminum battery case, and non-aqueous electrolyte wasinjected into the case. Then, the case was sealed. In this way, asecondary battery was fabricated.

Here, a mixture organic solvent of ethylene carbonate (EC), dimethylcarbonate (DMC), propylene carbonate (PC), and flurorobenzene (FB)(volumetric ratio of EC:DMC:PC:FB was 30:55:5:10), in which 1.1 M ofLiPF6 was dissolved, was used as the non-aqueous electrolyte.

Although specific type of materials (electrolyte, base layer, adhesivelayer, etc.) or parameters (thickness, width, shrinkage percentage,etc.) were used in the above example 1, it is expected thatsubstantially the same or similar benefits are obtained from other typeof materials or parameters discussed in connection with FIGS. 1-9. Thesame applies to other examples discussed below.

Comparison Example 1

Comparison Example 1 was performed using the same method as Example 1except that the PP film coated with the 15 μm thickness PMMA adhesivewas used as the sealing tape.

Comparison Example 2

The 35 μm OPS film coated with the 15 μm thickness PMMA adhesive wasused as the sealing tape.

Experimental Example 1 Measurement of Movement

Movement of a secondary battery manufactured in Example 1 and ComparisonExample 1 was measured using a drum test method, and the results wereshown in Table 1 and Table 2. A long diameter of the electrode assemblyof Example 1 was 17.03, and a long diameter of Comparison Example 1 was17.19. Here, 18 secondary battery samples were respectively used formeasuring the long diameters in Example 1 and Comparison Example 1.

In the drum test method, the secondary battery was disposed within adrum, and a vibration (66 RPM) was applied. At this time, a change of aninternal resistance (IR) of the secondary battery per unit time wasmeasured. If an increase of the IR exceeds 110% when compared to aninitial IR, it was determined to be inconsistent. The more time it takesto obtain a determination of defectiveness from the drum test, theinternal movement of the secondary battery was reduced. The movementpreventing effect was confirmed through the drum test results.

TABLE 1 Initial time 100 min 120 min 140 min 160 min IR IR increase IRincrease IR increase IR increase Example 1 12.0 12.5 104% 12.3 103% 12.3103% 0.0 — 1 2 11.9 12.6 106% 12.2 103% 12.6 106% 0.0 — 3 12.2 12.6 103%12.3 101% 12.4 102% 0.0 — 4 11.9 12.3 103% 12.3 103% 12.1 102% 0.0 — 511.9 12.3 103% 12.2 103% 12.3 103% 0.0 — 6 11.9 12.3 103% 12.3 103% 12.3103% 0.0 — 7 12.3 13.5 110% 12.7 103% 13.1 107% 0.0 — 8 12.3 12.9 105%12.8 104% 12.8 104% 0.0 — 9 12.3 13.0 106% 12.8 104% 12.9 105% 0.0 — 1012.3 12.8 104% 12.8 104% 12.8 104% 0.0 — 11 12.0 12.8 107% 12.5 104%12.8 107% 0.0 — 12 11.9 12.5 105% 12.4 104% 12.1 102% 0.0 — 13 12.3 12.8104% 12.7 103% 13.0 106% 0.0 — 14 12.0 12.8 107% 12.3 103% 12.5 104% 0.0— 15 12.3 12.8 104% 13.0 106% 12.4 101% 0.0 — 16 12.0 12.8 107% 12.4103% 12.8 107% 0.0 — 17 12.0 12.7 106% 12.8 107% 12.5 104% 0.0 — 18 12.012.6 105% 12.3 103% 12.7 106% 0.0 —

TABLE 2 Initial 60 min 80 min 100 min time in- in- in- IR IR crease IRcrease (%) IR crease Com- 1 16.2 17.3 107% 0.0 — — — par- 2 16.2 16.8104% 0.0 — — — ison 3 16.6 17.6 106% 17.3 104% 17.1 103% Exam- 4 16.317.3 106% 17.3 106% 17.3 106% ple 1 5 16.0 16.8 105% 0.0 — — — 6 16.016.7 104% 16.7 104%  0.0 — 7 15.7 16.8 107% 16.9 108% 17.2 110% 8 15.516.2 105% 16.4 106%  0.0 — 9 15.6 16.5 106% 0.0 — — — 10 15.4 16.3 106%16.3 106%  0.0 — 11 15.4 16.6 108% 16.7 108%  0.0 — 12 15.3 16.3 107%16.3 107% 16.8 110% 13 15.1 0.0 — — — — — 14 15.7 16.5 105% 0.0 — — — 1515.8 16.1 102% 0.0 — — — 16 15.6 16.2 104% 0.0 — — — 17 15.6 16.1 103%0.0 — — — 18 15.4 16.2 105% 0.0 — — —

As shown in Table 1 and Table 2, in the case of Comparison Example 1 towhich the PP film is applied, according to the drum test, defectivenessoccurs at about 60 min. However, in the case of Example 1 to which theshrinkable OPS film is applied, it can be observed that the drum testpassed at about 140 min. Thus, it can be observed that the secondarybattery to which the shrinkable OPS film according to the embodiments isapplied has a significantly improved movement preventing effect whencompared to Comparison Example 1 to which the existing general film isapplied.

Experimental Example 2 Measurement of Thickness Uniformity

To confirm thickness uniformity of the shrinkable OPS film of Example 1and the OPS film of Comparison Example 2, thicknesses were measured at acertain position to obtain standard deviation, and the results wereshown in Table 3. For reference, the thickness of the OPS film ofComparison Example 2 was measured using two textile samples.

TABLE 3 Measurement Comparison Example 2 Example 1 Number A: thicknessB: thickness thickness  1 0.028 0.033 0.040  2 0.031 0.03 0.038  3 0.0290.027 0.039  4 0.027 0.028 0.039  5 0.026 0.029 0.039  6 0.029 0.0260.041  7 0.027 0.029 0.039  8 0.026 0.028 0.039  9 0.026 0.025 0.040 100.029 0.033 0.040 11 0.03 0.026 0.040 12 0.03 0.027 0.040 13 0.028 0.0310.040 14 0.026 0.03 0.041 15 0.025 0.026 0.039 16 0.029 0.028 0.039 170.027 0.03 0.039 18 0.027 0.025 0.038 19 0.031 0.026 0.040 20 0.0310.025 0.040 21 0.029 0.032 0.041 22 0.03 0.031 0.038 23 0.028 0.0280.038 24 0.026 0.026 0.039 25 0.027 0.028 0.039 26 0.028 0.025 0.039 270.026 0.027 0.040 28 0.028 0.028 0.041 29 0.028 0.026 0.040 30 0.030.031 0.040 31 0.031 0.028 0.041 32 0.031 0.028 0.042 33 0.029 0.030.042 34 0.026 0.031 0.041 35 0.025 0.025 0.040 36 0.028 0.027 0.039 370.027 0.028 0.039 38 0.026 0.026 0.040 39 0.03 0.025 0.040 40 0.0310.026 0.039 41 0.028 0.031 0.040 42 0.03 0.03 0.041 43 0.029 0.028 0.04144 0.028 0.028 0.040 45 0.026 0.027 0.038 46 0.029 0.026 0.039 47 0.0270.028 0.039 48 0.028 0.029 0.038 49 0.028 0.026 0.038 50 0.031 0.030.039 51 0.031 0.027 0.040 52 0.031 0.027 0.041 53 0.027 0.029 0.040 540.027 0.029 0.040 55 0.026 0.026 0.041 56 0.027 0.028 0.040 57 0.0280.03 0.040 58 0.027 0.025 0.040 59 0.031 0.027 0.038 60 0.031 0.0250.039 Average 0.028 0.028 0.04 standard 0.00182 0.00213 0.00102deviation

As shown in Table 3, it can be observed that the shrinkable OPS film hassuperior thickness uniformity.

Experimental Example 3 Confirmation of Foreign Substances

Magnified photographs (×30) of OPS films of Example 1 and ComparativeExample 2 were analyzed, and analysis results are shown in FIG. 8 (OPSfilm of Comparative Example 2) and FIG. 9 (shrinkable OPS film ofExample 1).

As shown in FIGS. 8 and 9, it can be observed that a size of a foreignsubstance is small in the shrinkable OPS film of Example 1 according toan embodiment. A gel size of the shrinkable OPS film of Example 1 is inthe range of 0.5 mm to 1 mm, and a gel size of the shrinkable OPS filmof Comparative Example 2 is in the range of 0.5 mm to 15 mm. Inparticular, measurement results of thicknesses of the foreign substancesshowed that the gel thickness of the shrinkable OPS film of Example 1was 4 μm, and the gel thickness of the OPS film of Comparative Example 2was 45 μm.

Experimental Example 3 Confirmation of Adhesive Force

Adhesive forces of electrode assemblies of secondary batteries inExample 1 and Comparative Example 2 were measured, and results are shownin Table 4. The adhesive forces were measured in such a way that upperand lower parts of the prepared secondary cell were cut, a push-pullgauge was then placed at the lower part, and thereafter a force wasmeasured at the timing when the electrode assembly was shifted bypushing the push-pull gauge in an upper direction.

TABLE 4 Example 1 Comparative Example 2 Long Adhesive Force LongAdhesive Force Diameter (kgf/cm²) Diameter (kgf/cm²) 17.09 5.0 17.20 417.08 6.0 17.05 3 17.07 9.0 17.04 2.8 17.05 7.0 17.03 1.7 17.02 2.417.00 2.7 17.00 5.3 16.95 2.7

As shown in Table 4 above, it can be confirmed that Example 1 employingthe OPS film according to an embodiment is significantly better than theOPS film of Comparative Example 2 even though both of them have similarlong diameters (for example, see adhesive forces at the long diameter of17.05).

According to at least one embodiment, when the base sheet of the sealingtape contacts the electrolyte, the base sheet may lose itsdirectionality, and thus is shrunk and deformed. As a result, arelatively thicker portion generated through the above-described processcontacts the inner surface of the can to prevent the electrode assemblyfrom being moved within the can.

According to at least one embodiment, when the base sheet is shrunk, thebase sheet is separated from the adhesive layer. At this time, theadhesive layer is maintained in a state in which the adhesive layer isattached to the electrode assembly to provide a certain adhesive force.Thus, although the base sheet of the sealing tape is shrunk, theremaining adhesive layer may provide the certain adhesive force toprevent the electrode assembly from being released.

Exemplary embodiments have been disclosed herein, and although specificterms are employed, they are used and are to be interpreted in a genericand descriptive sense only and not for purpose of limitation. Forexample, the processing of embodiments may be implemented firmware or insoftware, e.g., by an article of manufacture having a machine-accessiblemedium including data that, when accessed by a machine, cause themachine to drive a battery management system. Accordingly, it will beunderstood by those of ordinary skill in the art that various changes inform and details may be made without departing from the spirit and scopeof the present invention as set forth in the following claims.

1. A secondary battery, comprising: an electrode assembly comprising anouter surface; an electrolyte; a sealing tape attached to andsurrounding at least part of the outer surface of the electrodeassembly, wherein the sealing tape comprises i) an adhesive layercontacting the outer surface of the electrode assembly and ii) a baselayer formed on the adhesive layer, and wherein the base layer is formedof a material which has directionality; and a can accommodating theelectrode assembly and sealing tape, wherein the base layer, uponcontacting the electrolyte, is configured to at least partially losedirectionality and partially shrink so that at least a portion of thebase layer is partially thicker than other portions of the base layer.2. The secondary battery of claim 1, wherein the adhesive layer, uponcontacting the electrolyte, is configured to not substantially deform soas to maintain the adhesive property thereof.
 3. The secondary batteryof claim 2, wherein the adhesive layer has an adhesion force rangingfrom about 2 kgf/cm² to about 9 kgf/cm².
 4. The secondary battery ofclaim 1, wherein at least a portion of the base layer is thicker than atleast a different portion of the base layer, and wherein the thickerportion of the base layer contacts an inner surface of the can.
 5. Thesecondary battery of claim 1, wherein the electrolyte comprise at leastone of the following: dimethyl carbonate (DMC), diethyl carbonate (DEC),dipropyl carbonate (DPC), methylpropylcarbonate (MPC), ethylpropylcarbonate (EPC), methylethyl carbonate (MEC), ethylene carbonate (EC),propylene carbonate (PC), and butylene carbonate (BC).
 6. The secondarybattery of claim 1, wherein the base layer has a thickness in the rangeof about 20 μm to about 60 μm.
 7. The secondary battery of claim 1,wherein the thickness of the adhesive layer is in the range of about 1μm to about 30 μm.
 8. The secondary battery of claim 1, wherein theadhesive layer comprises an acryl-based adhesive material, and whereinthe acryl-based adhesive material comprises at least one of thefollowing: poly methyl methacrylate (PMMA), poly ethyl methacrylate(PEMA), and poly butyl methacrylate (PBMA).
 9. A secondary battery,comprising: an electrode assembly comprising an outer surface; anelectrolyte; a sealing tape attached to and surrounding at least part ofthe outer surface of the electrode assembly, wherein the sealing tapecomprises i) an adhesive layer contacting the outer surface of theelectrode assembly and ii) a base layer formed on the adhesive layer;and a can accommodating the electrode assembly and sealing tape, whereinthe base layer comprises first and second regions, wherein the firstregion is thicker than the second region, and wherein the first regioncontacts an inner surface of the can.
 10. The secondary battery of claim9, wherein the thickness of the first region of the base layer is in therange of about 20 μm to about 300 μm.
 11. The secondary battery of claim9, wherein the base layer comprises at least one of the following:polystyrene (PS), polyamide, polyacrylonitrile, polyvinyl alcohol,polycarbonate, polyethylene vinyl acetate, and oriented polystyrene(OPS).
 12. The secondary battery of claim 9, wherein the adhesive layer,upon contacting the electrolyte, is configured to not substantiallydeform so as to maintain the adhesive property thereof.
 13. Thesecondary battery of claim 12, wherein the adhesive layer has anadhesion force ranging from about 2 kgf/cm² to about 9 kgf/cm².
 14. Amethod of manufacturing a secondary battery, comprising: providing 1) anelectrode assembly comprising an outer surface, 2) a sealing tapeattached to and surrounding at least part of the outer surface of theelectrode assembly, wherein the sealing tape comprises i) an adhesivelayer contacting the outer surface of the electrode assembly and ii) abase layer formed on the adhesive layer, wherein the base layer isformed of a material which has directionality and wherein the base layercomprises first and second regions, and 3) a can configured to receivethe electrode assembly and sealing tape; placing the electrode assemblyand the sealing tape into the can so as to form an assembled secondarybattery; and subjecting the base layer to contact electrolyte, whereinthe base layer at least partially loses directionality and partiallyshrinks so that the first region is thicker than the second region andcontacts an inner surface of the can.
 15. The method of claim 14,wherein the shrinkage of the base layer in an axial direction is greaterthan that in a winding direction, and wherein the axial direction issubstantially perpendicular to the winding direction.
 16. The method ofclaim 14, wherein the shrinkage of the base layer is about 40% or morewith respect to the base layer before contacting the electrolyte. 17.The method of claim 16, wherein the shrinkage of the base layer is inthe range of about 40% to about 64% with respect to the base layerbefore contacting the electrolyte.
 18. The method of claim 16, whereinthe shrinkage of the base layer in a axial direction is in the range ofabout 50% to about 70%, and wherein the shrinkage of the base layer in awinding direction is in the range of about 0% to about 5%.
 19. Themethod of claim 14, wherein the base layer has a thermal shrinkagecharacteristic under a temperature of about 30° C.
 20. The method ofclaim 14, wherein the electrolyte comprise at least one of thefollowing: dimethyl carbonate (DMC), diethyl carbonate (DEC), dipropylcarbonate (DPC), methylpropylcarbonate (MPC), ethylpropyl carbonate(EPC), methylethyl carbonate (MEC), ethylene carbonate (EC), propylenecarbonate (PC), and butylene carbonate (BC).
 21. The method of claim 14,wherein the base layer comprises a shrinkable oriented polystyrene (OPS)film.
 22. The method of claim 21, wherein the shrinkable OPS film ismanufactured using an elongation process.
 23. The method of claim 22,wherein the shrinkable OPS film has a shrinkage of about 40% or more.24. The method of claim 22, wherein a longitudinal elongation of the OPSfilm is over about 45% and a transverse elongation of the OPS film isover about 210%.
 25. The method of claim 14, further comprisingperforming at least one of a formation process and an aging process. 26.The method of claim 25, wherein the aging process is performed byexposing the assembled battery to an environment having a temperaturefrom about 50° C. to about 70° C. for about 18 hours to about 36 hours.27. The method of claim 14, wherein the adhesive layer, upon contactingthe electrolyte, does not substantially deform so as to maintain theadhesive property thereof, and wherein the adhesive layer has anadhesion force ranging from about 2 kgf/cm² to about 9 kgf/cm².